SP SERIES WELDING ELECTRODES

SP Series | SMAW Electrodes | Ador Fontech Ltd. Image Popup

SP SERIES WELDING ELECTRODES

SPEM 0010

Electrode for high strength and extreme crack resistance

TECHNICAL DATA

UTS: 67-87 kgf/mm2
Elongation (L=4D): 22-30%

TYPICAL APPLICATIONS

Heavy machinery parts, earth moving equipment parts, automobile springs, trunnions of cement mill & other allied components, parts subject to heat, corrosion & impact. Joining of high carbon, low & high alloy steels, tool steels, spring steels, manganese steels, case hardening steels, high speed steels, cast steels & for difficult to weld steels, unidentified steels & dissimilar steels. Also best suited for joining of such steels with one another. Also suitable for cushioning layer under hard deposits.

spem 0010
SPHF 043

Chromium-iron type alloyed electrode for good temperature and abrasion resistance

TECHNICAL DATA

Hardness: 57-62 HRC

TYPICAL APPLICATIONS

For applications where combination of toughness and hardness is desired. Hard surfacing of parts which are subject to severe abrasive wear and moderate shocks. Conveyor worm screws, mixer blades, auger screws, dredging cutters, bells & hoppers, runner bottom edges, etc.

sphf 043
SPSP 0050

A nickel base super – alloy electrode

TECHNICAL DATA

Hardness as welded 18 HRC
After work hardening 42 HRC

TYPICAL APPLICATIONS

For hard-facing of hot forging dies, hot working tools & hot shear blades. Joining of Nimonic and Inconel alloys and these alloys to alloy steel, carbon steel. For depositing corrosion resistant layer (cladding) on valves and pump components when wear and corrosion resistant surface is required.

spsp 0050
SPGW 0070

General purpose electrode for welding mild and structural steels

TECHNICAL DATA

UTS: 46-65 kgf/mm2
Elongation: 22-30%
Charpy V notch Impact value at 27ºC: 105 Joules

TYPICAL APPLICATIONS

Welding of IS 2062, IS 2002 Gr. A steels, structural steels having UTS in the range of 48 kgf/mm2. Sheet metals, bridges, steel structures, construction industries. For tack and intermittent welding. Railway wagons and coaches, pipes, steel furniture, etc.

spgw 0070
SPFI 0100

For repair of dies in forging industry

TECHNICAL DATA

UTS: 95-110 kgf/mm2
YS: 80-100 kgf/mm2
Hardness as welded: 26-36 HRC
Elongation: 14-16%

TYPICAL APPLICATIONS

Forging dies for filling all types of die impressions. Machinery parts made of high tensile steel material in earth moving equipment. Automotive parts and certain grades of armour steel, steam turbine rotors in service up to 540ºC. Repair of case hardening steel parts after removing the hard zone for repairing cracks in Ni-Cr hot working dies.

spfi 0100
SPAC 0400

Electrode for welding Inconel 600 and similar nickel base, composition alloys

TECHNICAL DATA

UTS: 62-78 kgf/mm2
Elongation: 28-32%
Impact strength at +20º C 100 J at -196ºC: 80 J

TYPICAL APPLICATIONS

Basic Flux coated nickel base electrode for welding Inconel 600, inconel, incoloy monel, nickelchromium- iron alloys, HK alloys, stainless and heat resisting steels. Also for welding dissimilar metals such as carbon steels, stainless steels, nickel and nickel alloys to each other. For use on equipment and components made of pure nickel for fabrication of corrosion resistant tanks and containers, heat exchangers, furnace components, fittings, etc. Highly suitable for a wide range of dissimilar joint combinations between nickel base alloys and low alloy steels.

spac 0400
SPCI 0600

Electrode for welding high strength nodular cast iron

TECHNICAL DATA

UTS: 32-43 kgf/mm2
Hardness 15-20 HRC

TYPICAL APPLICATIONS

Electrode has easy and intimate fusion behavior with all types of cast irons. Hence best suited for welding and repairing all cast iron components, pump casings, valve flanges, foundry defects, correcting machining errors on castings and joining cast iron to steel.

spci 0600
SPCP 2209

Electrode for welding corrosion resistant duplex stainless steels

TECHNICAL DATA

UTS: 70-84 kgf/mm2
Elongation: 30-35%

TYPICAL APPLICATIONS

For welding wrought, forged or cast duplex stainless steels for service in the as-welded condition. Offshore, oil/gas, chemical and petrochemical process industries e.g. pipe line systems, flow lines, risers, manifolds, etc.

spcp 2209