STAINLESS STEEL WELDING

Stainless Steel Welding | TIG/MIG/SAW Welding Services Image Popup

STAINLESS STEEL

TIG/MIG/SAW120

Cr-Ni austenitic stainless steel filler wire with controlled ferrite content for TIG/MIG/SAW welding processes for welding of Stainless steel

TECHNICAL DATA

UTS: 52-65 kgf/mm2
Elongation: 35-45%
Shielding Gas: Welding grade argon

TYPICAL APPLICATIONS

For joining and cladding AISI 304, 304 L stainless steels. For welds subjected to operating temperatures from -269 to +350ºC and requiring non-scaling properties up to 800ºC in air or in an oxidizing atmosphere of combustion gases. Welded joints in ferritic Cr steels (max. 18% Cr), only for root and intermediary runs if subjected to sulphurous gases. Suitable for steel grades Wnr. 1.4301, 1.4306, 1.4308, 1.4312, 1.4541, 1.4543, 1.550, 1.4552, 1.6901, 1.6902, 1.6903, 1.6905.

tigmigsaw120
TIG/MIG/SAW 120 H

Austenitic stainless welding rod /wire for welding AISI 304 with high carbon for welding of Stainless steel

TECHNICAL DATA

UTS : 55-64 kgf/mm2
Elongation : 35-45%

TYPICAL APPLICATIONS

For welding of austenitic stainless steels including high carbon type AISI 304 H in industries like petrochemicals, refinery, chemical and engineering. Very good welding and flow characteristics. Storage tanks, pipe lines, pumps, valves etc.

tigmigsaw 120 h
TIG/MIG 120 S

Austenitic, columbium-stabilized, stainless steel filler rod / wire for TIG/ MIG welding processes for welding of Stainless steel

TECHNICAL DATA

UTS: 52-64 kgf/mm2
Elongation: 35-45%

TYPICAL APPLICATIONS

For welding of 18% Cr / 8% Ni stainless steel or 18/8 SS stabilized with either columbium or Titanium. AISI 301, 302, 304, 321, 347, etc.

tigmig 120 s
TIG/MIG 120 SSi

Austenitic, columbium-stabilize, stainless steel filler rod/wire with higher silica for TIG/MIG welding processes for welding of Stainless steel

TECHNICAL DATA

UTS: 52-64 kgf/mm
Elongation: 30-35 %

TYPICAL APPLICATIONS

For welding of 18% Cr/8% Ni stainless steel or 18/8 SS stabilized with either columbium or Titanium. AISI 301, 302, 304, 321, 347, 347Si etc.

tigmig 120 ssi
TIG/MIG 120 Si

Austenitic stainless steel filler rod/wire for welding AISI 304L by TIG/MIG processes for welding of Stainless steel

TECHNICAL DATA

UTS: 55-60 kgf/mm2
Elongation: 35-45%
Impact energy (Charpy V): 120 J

TYPICAL APPLICATIONS

Suitable for joining stainless steels of the 18Cr/8Ni EL-type and 18Cr/8Ni/Nb type for service temperatures up to 350ºC.

tigmig 120 si
TIG/MIG/SAW 121

Austenitic Cr-Ni-Mo stainless steel filler rod/wire for TIG/ MIG/SAW welding processes for welding of Stainless steel

TECHNICAL DATA

UTS: 49-60 Kgf/mm2
Elongation: 30-40%
Shielding Gas: Welding grade argon (TIG); Argon + 1-2% oxygen (MIG)

TYPICAL APPLICATIONS

For chemical corrosion resistance and cryogenic steels. Suitable for steel grades Wnr. 1.4301, 1.4306, 1.4308, 1.4312, 1.4401, 1.4408, 1.4410, 1.4435, 1.4436, 1.4541, 1.4550, 1.4552, 1.4571, 1.4573, 1.4583, 1.4580 and 1.4581 as well as 1.4417, 1.6901, 1.6902, 1.6903, 1.6905. AISI 316, 316L etc. Chemical tanks, valves, pump bodies, agitator blades, impellers, pipelines etc.

tigmigsaw 121
TIG/MIG/SAW 121 Si

Austenitic Cr-Ni-Mo stainless steel filler rod/wire with higher silica for TIG/MIG/SAW welding processes for welding of Stainless steel

TECHNICAL DATA

UTS: 49-60 Kgf/mm2
Elongation: 30-40%
Shielding Gas: Welding grade argon (TIG); Argon + 1-2% oxygen (MIG)

TYPICAL APPLICATIONS

For chemical corrosion resistance and cryogenic steels. Suitable for steel grades Wnr. 1.4301, 1.4306, 1.4308, 1.4312, 1.4401, 1.4408, 1.4410, 1.4435, 1.4436, 1.4541, 1.4550, 1.4552, 1.4571, 1.4573, 1.4583, 1.4580 and 1.4581 as well as 1.4417, 1.6901, 1.6902, 1.6903, 1.6905. AISI 316, 316L, 316L Si etc. Chemical tanks, valves, pump bodies, agitator blades, impellers, pipelines etc.

tigmigsaw121 si
TIG/MIG/SAW 122

Fully austenitic stainless steel filler rod / wire for TIG / MIG / SAW welding processes for welding of Stainless steel

TECHNICAL DATA

UTS: 56-65 Kgf/mm2
Elongation : 30-40%
Shielding Gas: Welding grade argon

TYPICAL APPLICATIONS

For welding corrosion and heat resisting, 25 Cr / 20 Ni steels. Very well suited for weld surfacing. Non-scaling up to 1150ºC generally, up to approx. 1050ºC in oxidizing and up to approx. 650ºC in reducing sulphurous atmospheres. Suitable for welding steel grades Wnr. 1.2782, 1.4832, 1.4837, 1.4841, 1.4845, 1.4848, 1.4849.

tigmigsaw 122
TIG/MIG/SAW 123

Austenitic stainless steel filler rod/wire for welding dissimilar steels, AISI 309 SS by TIG/MIG/SAW processes for welding of Stainless steel

TECHNICAL DATA

UTS: 52-62 Kgf/mm2
Elongation: 30-40%

TYPICAL APPLICATIONS

For welding 25 Cr / 12Ni alloys in wrought or cast forms. Welding of 18 Cr / 8 Ni base metals when severe corrosion conditions exist. Also used in welding dissimilar metals, such as joining 18 / 8 to manganese steel. Applying sheet lining of 12 percent chromium steels to mild steel shells.

tigmigsaw 123
TIG/MIG/123 Si

Austenitic stainless steel filler rod/wire with higher silica for welding dissimilar steels, AISI 309 SS by TIG/MIG/SAW processes for welding of Stainless steel

TECHNICAL DATA

UTS: 52-62 Kgf/mm2
Elongation: 30-40%

TYPICAL APPLICATIONS

For welding 25 Cr / 12Ni alloys in wrought or cast forms. Welding of AISI 309 L Si, 18 Cr / 8 Ni base metals when severe corrosion conditions exist. Also used in welding dissimilar metals, such as joining 18 / 8 to manganese steel. Applying sheet lining of 12 percent chromium steels to mild steel shells.

tigmig123 si
TIG/MIG 123 L Mo

Austenitic stainless steel filler rod/wire for welding dissimilar steels and buffer layers for welding of Stainless steel

TECHNICAL DATA

UTS: 52-65 Kgf/mm2
Elongation: 30-40%

TYPICAL APPLICATIONS

Used for joining dissimilar steels with stainless steel of any type. Used as a buffer layer prior to surfacing with 316 L for corrosion resistant overlays. Higher tolerance to dilution than 309S92 increase range of applications, but note that the lower ferrite potential reduces tolerance to dilution compared with related electrodes. Used for dissimilar welds where lower ferrite value and higher ductility is required. Not recommended for structural applications where post weld heat treatment is to be carried out or for long term high temperature service above 400ºC.

tigmig 123 lmo
TIG/MIG/SAW 124

Fully austenitic stainless steel filler rod/wire for TIG/MIG/ SAW welding processes for welding of Stainless steel

TECHNICAL DATA

UTS: 52-62 Kgf/mm2
Elongation: 30-40%

TYPICAL APPLICATIONS

For welding of Er385, HV-9 A and HV-9 stainless steels and similar alloys for excellent resistance to various corrosive media and temperature. Used in pharmaceuticals, fertilizer and chemical industry components.

tigmig 124
TIG/MIG 125

Duplex stainless rod/wire for welding 2209 type duplex stainless steels

TECHNICAL DATA

UTS: 69-84 Kgf/mm2
Elongation: 20-30%

TYPICAL APPLICATIONS

Used for pipework and general fabrication in offshore oil, gas and chemical process industries. Suitable for standard duplex stainless steels UNS S3183 (wrought) J92205 (cast), ASTM F51, DIN, 1.4462, BS, 1501 318S13. Proprietary alloys such as Hy-Resist 22/5 (Avasta Sheffield), SAF 2205 (Sandvik), AF22 (Mannesmann), Uranus 45N (Creusot) can be welded using TIG/MIG 125.

tigmig 125
TIG/MIG 126

Austenitic stainless steel filler rod / wire for welding AISI 317 L base metals

TECHNICAL DATA

UTS: 52-65 Kgf/mm2
Elongation: 30-40%

TYPICAL APPLICATIONS

This molybdenum bearing type ER 317 L grade is suitable for welding ER 317 L type of stainless steels. Welding of AISI 317 L type, for severe corrosion applications involving sulphuric and sulphurous acids and their salts, for steel fabrications in which post-heat treatment is to be avoided, for joining stainless steel to low alloy and carbon steels.

tigmig 126
TIG/MIG 127

TIG/MIG filler rod/wire for welding 13% Cr stainless steels

TECHNICAL DATA

UTS: 52-63 Kgf/mm2
ELONGATION: 20%

TYPICAL APPLICATIONS

Stainless steel filler alloy for TIG/MIG welding of 13% Cr steels. Used for joining as well as hard-facing applications made of AISI 410 metal like turbine blades, guide vanes, pelton wheels etc.

tigmig 127
TIG/MIG 128

Ferritic stainless steel filler rod / wire for welding AISI 430 type base metal

TECHNICAL DATA

UTS: 45-68 Kgf/mm2
YS: 30-36 Kgf/mm2
Hardness at 20ºC: 16 RC
Shielding Gas: Pure Argon

TYPICAL APPLICATIONS

Welding of corrosion and heat resisting steel grades. Weld surfacing on sealing surfaces of gas, water and steam fittings operating at temperatures up to 450ºC. Non-scaling up to 900ºC in air and in an atmosphere of oxidizing or sulphurous combustion gases. Especially suitable for building up edges. Good resistance to attack by sea water, organic and inorganic acids (nitric acid, sulphuric acid).

tigmig 128
TIG/MIG 130

Austeno-ferritic Cr-Ni-Mn steel filler rod for TIG welding all types of steels

TECHNICAL DATA

UTS: 66-73 Kgf/mm2
Elongation: 22-24%
Impact energy: 52 J (ISO-V/20ºC)
Shielding Gas: Welding grade argon, helium

TYPICAL APPLICATIONS

Used for joining, medium, high carbon, low alloy and high alloy steels, tool steels, spring steels, manganese steels, case hardening steels, quenched steels, steel castings, die steels etc.

tigmig 130
TIG / MIG 133

Austenitic stainless steel filler rod / wire for joining manganese steels and stainless steels type AISI 307

TECHNICAL DATA

UTS: 59-65 Kgf/mm2; 40-52 Kgf/mm2
Elongation: 30-45%
Impact energy (20O CJ): > 90
Shielding Gas: Ar + 2% O2 or Ar + 5% Co2

TYPICAL APPLICATIONS

Used for joining dissimilar steels, armour plates, manganese steels and generally difficult to weld steels. Buttering before hard facing. Gives strong, ductile and tough austenitic deposit which work hardens from 12-32 RC. Can be used for mix welding where deposits have to be heated. The most versatile for dissimilar steels.

tigmig 133
TIG/MIG 133 Si

Austenitic stainless steel filler rod/ wire with higher silica for joining manganese steels & stainless steels type AISI 307, 307 Si

TECHNICAL DATA

UTS: 65-74 Kgf/mm2
YS: 37-49 Kgf/mm2
Elongation (L=4D): 30-38%
Shielding Gas: Ar + 2% O2 or Ar + 5% CO2

TYPICAL APPLICATIONS

Used for joining dissimilar steels, armour plates, manganese steels and generally difficult to weld steels. Buttering before hard facing. Gives strong, ductile and tough austenitic deposit which work hardens from 12-32 RC. Can be used for mix welding where deposits have to be heated. The most versatile for dissimilar steels.

tigmig 133 si
TIG / MIG 134

Austenitic stainless steel rods and wires for TIG/MIG welding

TECHNICAL DATA

UTS: 52-60 Kgf/mm2
Elongation (L=4D): 30-40%

TYPICAL APPLICATIONS

Welding of austenitic stainless steels, corrosion resistance parts like pipe lines, pump impellers, agitators, vacuum rotors, heat exchanger headers etc.

tigmig 134